Wire Gauge, Resistance, Cross Section & Current Table

NOTES:

1. Construction: C – Concentric; U – Unilay; R – Ropelay

2. Change of 3 AWG Numbers Doubles Resistance and Halves Weight

3. Properties of Copper:

a) Tensile Strength: Hardened copper: 478 N/mm² (47.8kgf/mm²) Annealed Copper: 239 N/mm² (23.9kgf/mm²)

b) Average Resistivity: 1.7241 microhm-cm at 20°C

c) Maximum Temperature: 200°C for SPC – 280°C for NPC – 155°C for TPC

AWG CONSTRUCTION DIAMETER (mm) AREA (mm²) WEIGHT (g/m) R Ω max (Ω/100m) at 20°C
4 133 x 0.455 R 6.48 21.62 197.9 0.09
6 133 x 0.361 R 5.14 13.61 124.9 0.14
8 1 x 3.26 3.26 8.37 74.38 0.21
133 x 0.287 R 4.09 8.6 79.02 0.22
10 1 x 2.59 2.59 5.26 46.77 0.35
37 x 0.404 C 2.8 4.77 44.43 0.38
91 x 0.254 U 2.7 4.61 42.22 0.43
12 1 x 2.05 2.05 3.31 29.46 0.55
19 x 0.455 C 2.27 3.09 28.66 0.59
37 x 0.320 C 2.22 2.98 27.88 0.61
45 x 0.300 C 2.45 3.18 28.27 0.58
91 x 0.203 U 2.15 2.95 27 0.65
13 1 x 1.83 1.83 2.63 23.36 0.7
14 1 x 1.63 1.63 2.08 18.45 0.88
19 x 0.361 C 1.8 1.94 18.04 0.94
19 x 0.361 U 1.7 1.94 17.14 0.94
27 x 0.300 C 1.8 1.91 16.98 0.94
37 x 0.254 C 1.78 1.88 16.67 0.97
61 x 0.203 U 1.76 1.97 18.5 1.04
15 1 x 1.45 1.45 1.65 14.68 1.11
16 1 x 1.29 1.29 1.31 11.62 1.4
19 x 0.287 C 1.42 1.23 11.41 1.49
19 x 0.287 U 1.36 1.23 10.83 1.49
19 x 0.300 C 1.5 1.34 12.5 1.36
19 x 0.300 U 1.43 1.34 11.86 1.36
61 x 0.16 U 1.45 1.23 11.23 1.45
315 x 0.071 R 1.6 1.25 11.8 1.47
17 1 x 1.15 1.15 1.04 9.24 1.76
18 1 x 1.02  1.02 0.824 7.32 2.22
7 x 0.404 1.21 0.901 8.25 2.03
19 x 0.254 C 1.27 0.962 8.93 1.9
19 x 0.254 U 1.21 0.962 8.49 1.9
61 x 0.142 U 1.24 0.966 9 1.89
19 1 x 0.91 0.91 0.653 5.8 2.8
20 1 x 0.813 0.813 0.518 4.61 3.53
7 x 0.320 0.96 0.563 5.17 3.25
19 x 0.203 C 1.009 0.616 5.7 2.97
19 x 0.203 U 0.966 0.616 5.42 2.97
37 x 0.142 U 0.97 0.586 5.38 3.12
135 x 0.071 0.92 0.534 4.9 3.42
21 1 x 0.724 0.724 0.412 3.66 4.44
22 1 x 0.643 0.643 0.324 2.89 5.64
7 x 0.254 0.762 0.355 3.26 5.15
19 x 0.160 C 0.8 0.382 3.55 4.78
19 x 0.160 U 0.762 0.382 3.37 4.78
37 x 0.114 U 0.78 0.38 3.46 4.83
72 x 0.071 0.68 0.285 2.6 6.41
23 1 x 0.574 0.574 0.259 2.3 7.06
24 1 x 0.511 0.511 0.205 1.82 8.91
7 x 0.203 0.609 0.227 2.08 8.05
19 x 0.127 C 0.634 0.241 2.23 7.58
19 x 0.127 U 0.597 0.241 2.12 7.58
56 x 0.071 U 0.6 0.222 2.05 8.23
25 1 x 0.455 0.455 0.163 1.44 11.24
26 1 x 0.404 0.404 0.128 1.14 14.26
7 x 0.160 0.48 0.141 1.29 12.96
19 x 0.102 C 0.504 0.155 1.44 11.79
19 x 0.102 U 0.483 0.155 1.37 11.79
33 x 0.071 U 0.45 0.13 1.2 14.06
27 1 x 0.320 0.361 0.102 0.91 17.86
28 1 x 0.320 0.32 0.08 0.72 22.72
7 x 0.127 0.381 0.089 0.82 20.6
19 x 0.079 C 0.395 0.093 0.86 19.63
29 1 x 0.287 0.287 0.065 0.58 28.25
30 1 x 0.254 0.254 0.051 0.45 36.07
7 x 0.102 0.304 0.057 0.53 31.95
19 x 0.063 C 0.315 0.059 0.57 30.87
31 1 x 0.226 0.226 0.04 0.36 45.56
32 1 x 0.203 0.203 0.032 0.29 56.47
7 x 0.079 0.237 0.034 0.32 53.28
19 x 0.050 C 0.25 0.037 0.36 49
33 1 x 0.180 0.18 0.025 0.23 71.82
34 1 x 0.160 0.16 0.02 0.18 90.9
7 x 0.063 0.189 0.022 0.21 83.8
35 1 x 0.142 0.142 0.016 0.14 115.4
36 1 x 0.127 0.127 0.0127 0.11 144.3
7 x 0.050 0.15 0.0137 0.13 133.4
37 1 x 0.114 0.114 0.0102 0.09 179
38 1 x 0.102 0.102 0.0081 0.07 225
7 x 0.040 0.12 0.0088 0.0784 214
39 1 x 0.089 0.089 0.00622 0.06 295
40 1 x 0.079 0.079 0.0049 0.0436 375
7 x 0.031 0.09 0.00528 0.0469 350
41 1 x 0.071 0.071 0.00396 0.0352 460
42 1 x 0.063 0.063 0.00316 0.0281 600
7 x 0.025 0.075 0.0034 0.0318 536
43 1 x 0.056 0.056 0.00246 0.0219 745
44 1 x 0.050 0.05 0.00203 0.018 910
7 x 0.020 0.06 0.0022 0.0196 836
46 1 x 0.040 0.04 0.00126 0.0112 1500
7 x 0.015 0.045 0.001372 0.0112 1492
48 1 x 0.031 0.031 0.00075 0.0067 2450
7 x 0.0125 0.0375 0.000859 0.0077 2371
50 1 x 0.025 0.025 0.00049 0.0044 3750
7 x 0.0100 0.03 0.00055 0.0049 3872
52 1 x 0.020 0.02 0.00031 0.0028 5850
54 1 x 0.0158 0.0158 0.000196 0.00175 10441
56 1 x 0.0125 0.0125 0.000123 0.00109 16599
58 1 x 0.0100 0.01 0.000079 0.0007 27101